Brass EDM Wire and Zinc Coated Wire Electrode Wire for EDM Machine

Brass Wire & Zinc Coated Wire
0.20mm & 0.25mm P5 / K160 / K200
TAGUTI Factory High Quality

Chat Now
Product Details

TAGUTI® EDM Brass Wire:

This TAGUTI® brass wire draws its properties from high grade alloy. The excellent tensile strength of the wire, as well as the exceptional surface property, improves significantly the cutting precision. It is made by normal brass alloy to be used normal machine condition at WEDM. The auto threading rate can be raised whether the threading mechanism is pipe type, water jet type, or anneal cutting type because the wire is very straight. Also, the surface is treated to prevent brass powdering. This TAGUTI® wire is suitable in particular for Fanuc, Hitachi, Mitsubishi and Sodick machines. To meet the market demands, TAGUTI introduces this brass wire with most application and higher cost-performance.

 

TAGUTI® Features:

Suitable for automatic threading

Exceptional tensile strength

Extreme cleanness of the wire

High reliability during machining

Obtains excellent surface finish

Recommended for high precision work

 

Basic Information:

Brass Wire
Characteristics
Diameter
KG/Roll

TAGUTI®

EDM Brass Wire

Core
CuZu35

φ0.20mm

φ0.25mm

φ0.30mm

5.0KG
Tensile Strength
900N/mm² (Hard)
Elongation
<3% (Hard)
Conductibility
20% IACS
Surface Color
Golden

 

Brass Wire Samples:

TAGUTI® brass wire


Zinc Coated Wire From TAGUTI (Brass Core & Zinc Coating)

This is a coated TAGUTI brass wire developed in response to a market demand for high quality and precision wire. It is particularly suitable for applications with special requirements for extremely fine precision cuts. The special coating ensures a very clean finish along the cut surfaces as well as a high performance in terms of cutting speed. Compared with brass wire, this TAGUTI type coated wire has faster cutting speed and improves surface roughness and dimension precision. Also, this zinc coated wire guarantees stable conductivity.

 

TAGUTI® Features:

High precision in cutting

Excellent surface finish - Ra 0.1μm

Suitable for automatic threading

Cutting speed up to 20% faster than brass wire

Uses standard zinc coated technology

High speed erosion, up to 10% faster than brass wire

 

Basic Information:

Coated Wire
Characteristics
Diameter
KG/Roll

AGIE

Cobra CUT A

Core
CuZu37

φ0.10mm

φ0.15mm

φ0.20mm

φ0.25mm

1.6KG

6.0KG

16KG

CoatingZu
Tensile Strength900N/mm² (Hard)
Elongation
<2%
Conductibility21% IACS
Surface Color
Silvery


Coated Wire
Characteristics
Diameter
KG/Roll

AGIE

Cobra CUT D

Core
CuZu20φ0.25mm
16KG
Coating
CuZu50
Tensile Strength
800N/mm² (Hard)
Elongation
<3%
Conductibility29%
Surface ColorBrown


Coated Wire
Characteristics
Diameter
KG/Roll

Charmilles

SWA

Core
CuZu37

φ0.10mm

φ0.25mm

3.7KG

15KG

Coating
Zu
Tensile Strength
900N/mm² (Hard)
Elongation
<2%
Conductibility21%
Surface ColorSlivery


Coated Wire
CharacteristicsDiameterKG/Roll

Charmilles

SWX

CoreCu

φ0.25mm

φ0.30mm

3.7KG

8.0KG

CoatingCuZu50
Tensile Strength510N/mm² (Half Hard)
Elongation<8%
Conductibility21%
Surface ColorBrown